عنوان انگلیسی Preparation of Cobalt Oxide/Zinc Oxide Nanocomposite
چکیده انگلیسی مقاله Cobalt Oxide/ Zinc Oxide nanocomposite was synthesized by dropwise addition ofCo(NO)3.6H2O and Zn(NO3)2.4H2O solutions to KOH solution at different temperatures followed bycalcination at 300ºC for 4 h. The morphology and structure of nanoparticles and the influence oftemperature on particle size were studied using scanning electron microscopy (SEM) and X-RayDiffraction (XRD). Minimum particle size was obtained before calcination at 70ºC. In addition, thespherical, semispherical and flake-shaped nanoparticles were observed at ambient temperature. Onthe other hand, Co(OH)2 was transformed to Co3O4, ZnO flakes were eliminated, and particle sizechanged during calcination. Synthesized samples at 50ºC and 70ºC showed an increase size aftercalcinations; however, elimination of flakes during calcination caused particle size reduction forsynthesized sample at ambient temperature.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله S. Alibeigi |
materials department, KNTU

M.R. Vaezi |
Nanotechnology and Advanced Materials Department, Material and Energy Research Center(MERC)

L. Nikzad |
Research Center of Advanced Materials, Merc

A. Esmaielzadeh Kandjani |
Applied Science, RMIT - RMIT University

نشانی اینترنتی http://www.ije.ir/article_71845_a91c606002eca76d53440ed34f8103d0.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2422121.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات