عنوان انگلیسی Fracture resistance of pulpotomized and composite‑restored primary molars: Incremental versus bulk‑fill techniques
چکیده انگلیسی مقاله Background: The aim of this study was to assess the fracture resistance of pulpotomized primary molars restored with incremental and bulk‑fill composite application techniques. Materials and Methods: In this in‑vitro experimental study, 36 extracted primary molars were nonrandomly (selectively) divided into three groups of 12 each. All teeth underwent conventional pulpotomy treatment, and mesio‑occluso‑distal cavities were prepared in such a way that the buccolingual width of the preparation was two‑thirds of the intercuspal distance, and the depth of the buccal and lingual walls was 4 mm. The teeth were then restored as follows: Group 1 (control) was restored with amalgam, Group 2 was restored with Tetric N‑Ceram composite using the incremental technique, and Group 3 was restored with Tetric N‑Ceram composite using the bulk‑fill technique. The restored teeth were subjected to thermocycling and then underwent fracture resistance testing in a universal testing machine at a crosshead speed of 1 mm/min. Fracture resistance of groups was compared using the one‑way ANOVA and Tukey’s honestly significant difference test. Results: The mean fracture resistance was 1291.47 ± 603.88 N in the amalgam, 1283.08 ± 594.57 N in the Tetric N‑Ceram incremental, and 1939.06 ± 134.47 N in the Tetric N‑Ceram bulk‑fill group. The difference in this regard between Group 3 and Groups 1 and 2 was statistically significant (P = 0.019 and P = 0.035, respectively). Conclusion: Bulk‑fill composite is recommended for reinforcing the remaining tooth structure after the primary molar pulpotomy procedure. Time‑saving characteristics of this material are clinically important for reducing appointment time for children. Key Words: Bulk‑fill composite, conventional composite, fracture resistance, primary molar,pulpotomy
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله | Masoud Fallahinejad Ghajari


| Amir Ghasemi


| Arash Yousefi Moradi


| Khashayar Sanjari


نشانی اینترنتی http://drj.mui.ac.ir/index.php/drj/article/view/2152
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article(s)
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات