عنوان انگلیسی Effect of NOCOLOK® Flux Dry-off Temperature on Mechanical Properties of Brazed Joint of Automotive Aluminum-Based Heat Exchangers
چکیده انگلیسی مقاله Drying temperature of the flux at normal atmosphere has a crucial role in brazing quality in automotive aluminum-based heat exchangers. Over the course of this research, NOCOLOK® flux consists of two phases of K2AlF5.H2O and KAlF4 with melting point around 580 °C was used. A flux slurry was applied on the base metal, and dried at 220, 300 and 380 °C in air. Mechanical assessment revealed that when flux dried at 300 °C, the joint withstands maximum shear stress of 44 MPa with complete bonding. At 220 °C and 380 °C, joint shear stresses are 34 MPa, 30 MPa respectively. 380 °C dry-off temperature under nitrogen gas improved shear strength to 39 MPa. Taking dry-off temperature as 300 °C the amount of defective heat exchangers was reduced from 6% to 2% on a daily basis.  
کلیدواژه‌های انگلیسی مقاله Brazing of Aluminum, NOCOLOK® Flux, Aluminum-Silicon
نویسندگان مقاله | Seyyed Ali Akbar Hashemi Milani
sahand university of technology


| Reza Tavangar
sahand university of technology


| Maziyar Azadbeh
sahand university of technology


| Ibrahim Kahinpoor
Iran Radiator Co.


| Hossein Sadeghi-Nasab
Iran Radiator Co.
نشانی اینترنتی http://www.iust.ac.ir/ijae/browse.php?a_code=A-10-444-1&slc_lang=en&sid=1
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده ساخت
نوع مقاله منتشر شده پژوهشی
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات