Iranian Journal of Materials Forming، جلد ۸، شماره ۳، صفحات ۴-۱۷
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Hot Deformation Behavior and Development of Constitutive Equations on a Novel γ-γ/ Ni-base Superalloy: AD730
چکیده انگلیسی مقاله In this work, hot deformation behavior and microstructural evolution for a novel Ni-base superalloy, AD730, were analyzed using a hyperbolic sine constitutive equation. The hot compression tests were carried out at a wide range of temperatures (950ºC-1200ºC) and strain rates (0.001-1 s-1). The modeling was done at the overall deformation conditions, and then the obtained important constitutive parameters, i.e., n and Q, were calculated to be 5.44 and 820.26 kJ/mol, respectively. Microstructural evolution showed two distinct domains at higher temperatures (1100ºC, 1150ºC, and 1200ºC) and lower ones (950ºC, 1000ºC, and 1050ºC) accomplished by dynamic recrystallization (DRX) and non-DRX behavior due to absence and presence of γ/ particles, respectively. Furthermore, the constitutive equations were analyzed based on both separated temperature domains. The obtained parameters from this approach demonstrated better results as compared with the literature, i.e., the parameters of n and Q were calculated to be 8.60 and 1160.45 kJ/mol at the lower domain, in contrast with 3.69 and 468.32 kJ/mol which were at higher ones. Additionally, the stress prediction data based on correlation coefficient factor (R2) presented the best reliable prospective at two separated domains as 0.994, as compared with overall conditions prediction with 0.963. It was found that hot working of AD730 alloy as well as flow stress can be essentially affected by the γ/-phase. Therefore, the hot deformation behavior of AD730, as a γ/-containing superalloy, should be performed at identified domains considering the solution temperature of γ/-phase.
کلیدواژه‌های انگلیسی مقاله AD730, Hot deformation, DRX, Hyperbolic sine modeling, γ/ phase
نویسندگان مقاله Zahra Mirzaie |
Materials and Polymers Engineering Department, Faculty of Engineering, Hakim Sabzevari University, Sabzevar, Iran

Gholam Reza Ebrahimi |
Materials and Metallurgical Engineering Department, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran

Hamidreza Ezatpour |
Department of Engineering Sciences, Hakim Sabzevari University, Sabzevar, Iran

Saeed Ali Akbari Sani |
Materials and Polymers Engineering Department, Faculty of Engineering, Hakim Sabzevari University, Sabzevar, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_6264_5803fb71baac9a890bf2eba120a855ae.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات