Iranian Journal of Materials Forming، جلد ۸، شماره ۲، صفحات ۴۴-۵۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Hot Workability and Processing Map of High Gd Content Mg-Gd-Zn-Zr-Nd Alloy
چکیده انگلیسی مقاله Hot workability of as-extruded high Gd content Mg-5Gd-0,5Zn-0.5Zr-2.5Nd alloy was investigated using the hot compression test in a temperature range of 300-500 °C and strain rates of 0.001-1s-1. Hot workability assessment was conducted by capturing microstructural evolution of high temperature deformed samples, and by constructing power dissipation and instability maps. Using experimental data of hot compression tests, the power dissipation map of the alloy was constructed, in which a domain of dynamic recrystallization (DRX) occurred at the temperature range of 350-450 °C and strain rate of 0.001-0.1 s-1, representing the optimum hot working window. Furthermore, the processing map of the alloy was constructed, and flow instability regions were also indicated based on the Ziegler's flow instability criterion.
کلیدواژه‌های انگلیسی مقاله Magnesium alloy, Rare earth metals, Processing map, Hot workability
نویسندگان مقاله Sahar Mosadegh |
Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran, Iran

Mehrdad Aghaie-khafri |
Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran, Iran

Behzad Binesh |
Department of Materials Science and Engineering, University of Bonab, ‎Bonab, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_6079_4a9dbf30c9ad8ea1604ccf816ec12e07.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات