Polyolefins Journal، جلد ۸، شماره ۲، صفحات ۶۳-۷۲
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Optimization of 1,3-butadiene monomer coordination polymerization using response surface methodology (RSM)
چکیده انگلیسی مقاله Laboratory runs can be minimized via experimental design which yields the optimum and best data regarding the independent parameters. In this research work, response surface methodology (RSM) based on a threelevel central composite design (CCD) was utilized to optimize and evaluate the interactive effects of processing conditions for polymerization of 1,3-butadiene (Bd) diene monomer using Ziegler-Natta catalyst. The polybutadiene rubber (PBR) having different cis content and molecular weight was obtained. The catalyst components included neodymium versatate (NdV3) as catalyst, triethyl aluminum (TEAL) as cocatalyst or activator, and ethylaluminum sesquichloride (EASC) as chloride donor. For the modeling, three independent variables, namely monomer concentration (8-28 wt%), reaction time (1.5-2.5 h), and reaction temperature (45-75ºC) at three levels were selected to optimize the dependent variables or responses including monomer conversion, viscosity-average molecular weight and the cis isomer content of the obtained polymer. The interaction between three crucial parameters was studied and modeled. Quadratic models were obtained to relate process conditions to dependent variables. It was observed that the optimal conditions predicted by RSM were consistent with the experimental data. Statistical analysis demonstrated that concentration of the monomer and the time of reaction significantly affected cis content. Moreover, processing conditions to achieve the desired response variables were predicted and experimentally approved. The optimal reaction conditions derived from RSM are monomer concentration = 19 wt%, polymerization time = 2 hours, and polymerization temperature = 50ºC. Polymerization was carried out at optimum conditions. The appropriate level of dependent variables including 94.2% monomer conversion, 151812 g/mol viscosity-average molecular weight and 98.8% cis content was acquired.
کلیدواژه‌های انگلیسی مقاله Ziegler-Natta, polybutadiene rubber, Processing conditions, Neodymium versatate, Response surface method
نویسندگان مقاله Ahmad-Ali Shokri |
Faculty of Polymer Engineering, Sahand University of Technology, P.O. Box: 51335-1996, Tabriz, Iran

Saeid Talebi |
Faculty of Polymer Engineering, Sahand University of Technology, P.O. Box: 51335-1996, Tabriz, Iran

Mehdi Salami-Kalajahi |
Faculty of Polymer Engineering, Sahand University of Technology, P.O. Box: 51335-1996, Tabriz, Iran

نشانی اینترنتی http://poj.ippi.ac.ir/article_1772_b749fc84c59a12da8e3dd98651364360.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات