عنوان انگلیسی Simple Preparation as well as Structural, Microstructural and Optical Properties of Cu Doped ZnO Nanostructures
چکیده انگلیسی مقاله In this study, the nanostructures of Zn1-xCuxO with x=0.000, 0.025, 0.050 and 0.075 were successfully synthesized by sol-gel auto combustion method using glycine as a fuel. The prepared powders were calcined at 300 °C. The effect of Cu doping on structural and optical properties of powders was studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible absorption spectroscopy (UV- vis) and photoluminescence (PL). The XRD patterns showed all samples have wurtzite structure. There is an extra peak belong to CuO at 2θ=38o in the XRD pattern of the sample with x=0.075. The average crystal size of the prepared powders is about 29-47 nm. The SEM micrographs revealed that all doped nanostructures have Leaf-like structure with the thickness about 15-20 nm. Absorption spectra showed a red shift and decrease in the band gap in the Zn1-xCuxO system. The PL spectra showed that the maximum Emission wavelength increases with dopant concentration.
کلیدواژه‌های انگلیسی مقاله Cu-doped ZnO, Nanosheets, Nanostructure, Optical absorption, Sol-Gel
نویسندگان مقاله Reavan Ghafouri Kesbi |
Department of Physics, Faculty of Science, Malayer University, Malayer, Iran

Hamed Bahiraei |
Department of Physics, Faculty of science, Malayer University, Malayer, Iran

Davood Ghanbari |
Department of Science, Arak University of Technology, Arak, Iran

نشانی اینترنتی https://jns.kashanu.ac.ir/article_111972_6e252683e886ef534d4afdaaa2066fde.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات