عنوان انگلیسی Tailoring of Eco-Friendly Epoxies with Synergistic Adhesion Strength
چکیده انگلیسی مقاله For sustainable development, eco-friendly epoxies, composed of recycled rubber micro-particles and core-shell rubber (CSR) nanoparticles, were processed to improve adhesion strength of an epoxy resin to structural steel substrates. To achieve this, the influence of mixing ratio of a recycled rubber micro-particles and CSR nanoparticles on the adhesion strength and adhesion fracture mechanisms of an epoxy were investigated in the present study. Synergistic adhesion strength was obtained for a certain combination of 7.5 parts per hundred resin (phr) CSR nanoparticles and 2.5 phr recycled rubber micro-particles. The remarkable increase in adhesion strength was attributable to “branching” of the crack-tip damage zone plus crack deflection to cause an adhesive to cohesive fracture transformation.
کلیدواژه‌های انگلیسی مقاله Recycled scrap tire, Nanoparticle, Epoxy, Adhesion strength, Micromechanisms
نویسندگان مقاله B. T. Marouf |
Department of Materials Science and Engineering, Faculty of Engineering, Urmia University, P. O. BOX 575615-1818, Urmia, Iran

R. Lesan-Khosh |
Baspar Pishrafteh Sharif Company, Tehran, Iran

R. Bagheri |
Department of Materials Science and Engineering, Sharif University of Technology, P. O. Box 11155-9466, Tehran, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_6856_8a870835367d5541fa1a9b3b8863e21d.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات