عنوان انگلیسی Effect of Graphite Addition on the Microstructure, Mechanical Properties and Oxidation Resistance of HfB2-SiC Composites Prepared by the SPS Method
چکیده انگلیسی مقاله In this study, HfB2-SiC-graphite composites were fabricated using spark plasma sintering at 1900 ℃ for 10 min. The effect of graphite content on the microstructure and mechanical properties was studied; also, oxidation resistance of the prepared composites was investigated at 1400 ℃ for 32 h. Weight changes and thickness of the formed oxide layer were measured. The relative density, toughness and strength of the SPSed composites increased with raising graphite up 2.5 wt% and then decraesed.  On the other hand, the hardness of the composites was decreased when graphite was added. Oxidation resistance of the composites was, thus, improved following graphite addition up 2.5 wt%, while the ecessive quantity of graphite caused poor oxidation resistance of the composites.
کلیدواژه‌های انگلیسی مقاله HfB2-SiC composite,Spark Plasma Sintering,Ultra-high Temperature Ceramic,oxidation,Graphite
نویسندگان مقاله M. Sakvand |
Faculty of Chemical and Materials Engineering, Shahrood University of Technology, Shahrood, Iran

M. Shojaie-Bahaabad |
Faculty of Chemical and Materials Engineering, Shahrood University of Technology, Shahrood, Iran

L. Nikzad |
Department of Ceramics, Materials and Energy Research Center, Karaj, Iran

نشانی اینترنتی https://www.ije.ir/article_150152_ba62dc91a64afda75038dcc36278af5c.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات