International Journal of Engineering، جلد ۳۵، شماره ۹، صفحات ۱۷۳۵-۱۷۴۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Effect of Friction Stir Processing on Fusion Welded Joint of Al-5083
چکیده انگلیسی مقاله Tungsten Inert Gas Welding (TIG) is the most preferred joining process for aluminum alloys, but it produces weld joint having inferior mechanical property in comparison with base metal because of inherent limitations of the process. To improve the mechanical properties, the weld is post processed by friction stir processing (FSP) upto depth of 2mm. This paper presents the effect of performing FSP on autogenous TIG welded butt joint of Al-5083, 6mm thick plate. Mechanical and metallurgical properties of both processed and unprocessed autogenous TIG weld are compared. Characterisation techniques adopted to evaluate weld joint are tensile test, microhardness measurement, microstructural examinations and SEM analysis. Tensile strength of autogenous TIG weld joint is lowered by 6.5% compared to base metal because of presence of micro porosities in the weld metal. Friction stir processing produces the fine grain refined structure, marginally improves the tensile strength of the autogenous TIG weld joint by 2.7%. Microhardness of the autogenous TIG weld metal of the surface is raised from 163.6 HV to 298 HV after performing FSP. However, SEM images of fractured surface of friction stir processed specimen reveals fine dimpled structure which indicates that ductility of the weld joint remain unaffected after performing FSP on autogenous TIG weld joint.
کلیدواژه‌های انگلیسی مقاله Friction Stir Processing,Surface modification,Autogenous TIG welding,Grain refinement
نویسندگان مقاله K. D. Tandel |
Sardar Vallabhbhai National Institute of Technology, Surat, India

J. V. Menghani |
Sardar Vallabhbhai National Institute of Technology, Surat, India

نشانی اینترنتی https://www.ije.ir/article_150452_d94e5798681e6ea260fe5430775141ec.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات