عنوان انگلیسی ModeI fracture toughness of Carbon/glass hybrid comopsite
چکیده انگلیسی مقاله Mode I fracture toughness of carbon/ glass reinforced polyster hybrid composite was invesitigated expermrntally and numerically by using the cosmos)/m 2.6 finite element software (fms) by utulizing the hand laup techniqe)(HLU). The single edge notch bending (SENB) test was developed to evalute the mode l fracture toughness of carbon composites, glass composite and hybrid compodite materials at varuos fiber configurations. Scaning electron microscope (SEM) was used to examine the fracture surface of the hybrid composite material under the effect of mode l loading. the expermental result showed the maximum stress intensity (sif) factor 882mpa. mm1/2. obtained in the hybrid composite with stacking dequencess (c/g/g/c) during the mode l loading compared to other stacking sequences. this is attributed to the goid interfical between the carbon and glass fibers and matrix face. From the resukts, it was suggested that the expermental results is a goid a gremnent with the finite element modelling
کلیدواژه‌های انگلیسی مقاله Fracture toughness,Hybrid Composites,hand layup techniqe,single edge notch bending
نویسندگان مقاله M. S. El-Wazery |
Department of Production Engineering and Mechanical Design, Faculty of Engineering, Menoufia University, Shebin El-Kom, Egypt

نشانی اینترنتی https://www.ije.ir/article_137172_13340b897ccca568011f7f51c3994064.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات