عنوان انگلیسی Synthesis and Characterization of Fe-Al2O3 Nanoparticles Prepared by Coprecipitation Method
چکیده انگلیسی مقاله In this study, iron-doped alumina (Fe-Al2O3) nanoparticles (NPs) containing 2 mol%, 4 mol%, and 6 mol% iron impurities were fabricated by the co-precipitation method in the presence of Al2(SO4)3.9H2O and Fe2(SO4)3.9H2O precursors. The prepared nanoparticles were heated at 1000 oC to study their physicochemical properties. The XRD results pointed out the multiphase for the samples. The morphological results revealed that the uniformity increased by increasing iron atoms rate. TEM analysis revealed that the particle with a size of 40 nm was obtained for 4% of the sample. The results of FT-IR analysis indicated that when the 2% impurity increases the AlO4 tetrahedra and AlO6 octahedral vibrational bond grow.
کلیدواژه‌های انگلیسی مقاله Fe-doped Al2O3,Nanocrystals,Coprecipitation method,Optical Properties,catalyst,Ceramics materials
نویسندگان مقاله Majid Farahmandjou |
Department of Chemistry, Faculty of Pharmaceutical Sciences, Tehran Medical Sciences, Islamic Azad University ,Tehran, I.R IRAN

Abolfazl Khodadadi |
Department of Physics, Tehran North Branch, Islamis Azad University, Tehran, I.R. IRAN

Mojtaba Yaghoubi |
Departments of Physics, Islamic Azad University, Ayatollah Amoli Branch, Amol, I.R. IRAN

نشانی اینترنتی https://ijcce.ac.ir/article_38036_a3fae4cea6adf9140deeb728a7b0533e.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات