Physical Chemistry Research، جلد ۱۰، شماره ۴، صفحات ۵۳۷-۵۴۷
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Effect of PVA/PEG-coated Fe3O4 Nanoparticles on the Structure, Morphology and Magnetic Properties
چکیده انگلیسی مقاله Iron oxide (Fe3O4) nanoparticles (NPs) are the most important group of magnetic nanoparticles. This study modifies iron oxide (Fe3O4) magnetic nanoparticles (MNPs) by polyethylene glycol (PEG) and polyvinyl alcohol (PVA) coating co-precipitation method. MNPs were characterized by XRD, FTIR, TEM, DLS, and VSM analyses to study their structure, morphology, and magnetic properties. The results showed the superior properties of PEG and PVA-coated Fe3O4 compared to the pristine sample. It is illustrated that modified Fe3O4 MNPs improved magnetic saturation. The particle size of PEG-coated Fe3O4 nanoparticles was estimated at 11 nm with magnetic saturation of 60.98 emu/g and coercivity of 8.26G.
کلیدواژه‌های انگلیسی مقاله Fe3O4 nanoparticles,PVA/PEG coating,Superparamagnetic,Co-precipitation method
نویسندگان مقاله Abolfazl Khodadadi |
Department of Physics, Tehran North Branch, Islamic Azad University, Tehran, I. R. Iran

Mohamad Rahim Talebtash |
Department of Engineering Shahriar, Branch Islamic Azad University, Shahriar, Iran

Majid Farahmandjou |
Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, Iran

نشانی اینترنتی https://www.physchemres.org/article_148292_fbe8e9996ea73393cdfc381a1f918a35.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات