Physical Chemistry Research، جلد ۱۰، شماره ۲، صفحات ۲۶۷-۲۷۱
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Structural and Morphological Studies on Strontium Tin Phosphate SrSn(PO4)2 Nanopowder
چکیده انگلیسی مقاله Strontium Tin phosphate SrSn(PO4)2 nanopowder was prepared by simple Solid State Reaction method (SSR). Structural and morphological investigations of the synthesized nanopowder were characterized by Powdered X-ray diffraction study (P-XRD), Fourier transform infrared (FT-IR) Spectroscopy, Field Emission Scanning Electron Microscopy (FE-SEM) and Energy Dispersive X-ray Spectroscopy Analysis (EDS). The average crystallite size estimated from P-XRD study was around 17 nm. W-H plot method was also agreed the size of the crystallite of the prepared sample in nanoscale. FE-SEM images show agglomerates of non-uniform biscuit like nano flakes structure. Various functional groups of prepared sample exhibited phosphate related bands are confirmed by FT-IR study.
کلیدواژه‌های انگلیسی مقاله Solid-state reaction method,Nanopowder,Strontium tin phosphate
نویسندگان مقاله Y Nirmal Rajeev |
Dept of Physics, Acharya Nagarjuna University, Guntur 522 510, India. Dept of Physics, V.R. Siddhartha Engineering College, Vijayawada 520 007, India

Venkatarao K |
Dept of Physics, Acharya Nagarjuna University, Guntur 522 510, India. Dept of Physics, Government Polytechnic College, Krosuru 522 410, India

B.V. Naveen Kumar |
Dept of Physics, Acharya Nagarjuna University, Guntur 522 510, India. Dept of Physics, BVC College of Engineering, Rajahmundry 5333 102, India

L. Bhushan Kumar |
Dept of Physics, Acharya Nagarjuna University, Guntur 522 510, India

Sandhya Cole |
Dept of Physics, Acharya Nagarjuna University, Guntur 522 510, India

نشانی اینترنتی https://www.physchemres.org/article_140886_079d54f6c8fc04a29cc43e67cfaf4f67.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات