عنوان انگلیسی The Effects of Silicon Oxide on the Structure, Physical Chemistry Properties, and Bioactivity of Phosphate Glasses Containing Sodium, Strontium, and Titanium Oxides
چکیده انگلیسی مقاله Glasses with molar compositions 40Na2O - 10SrO - (20-x)TiO2 - xSiO2 - 30P2O5 (0 ≤ x ≤ 10), corresponding to the chemical formula Na4Sr0.5Ti(1-y)Siy(PO4)3 ( 0 ≤ y ≤ 0.5) with O/P = 4, have been prepared by the classical melt - quenching technique and structurally characterized by XRD, DSC, FTIR, Raman, NMR and density measurements. The introduction of SiO2 in the phosphate glass weakens slightly the glass network, as shown by the low increase of the molar volume (VM) and the decrease of the glass transition temperature (Tg). This behaviour is due to the existence of more ionic P-O-Si bonds than the P-O-P bonds. Spectroscopy studies reveal that SiO2 behaves as network former like P2O5 oxide and the glass structure contains P-O, P-O-P, Si-O, Si-O-Si, Ti-O, Ti-O-Ti, P-O-Ti and P-O-Si linkages. The preliminary results of the in vitro bioactivity tests show the existence of ionic exchanges between the SBF solution and the studied glasses. X-ray powder diffraction and FTIR spectroscopy confirmed the formation of Ca-P layer on the surfaces of the tested compositions.
کلیدواژه‌های انگلیسی مقاله phosphate,Glass,Bioactivity,Raman,NMR
نویسندگان مقاله El Abdouni Ibtissam |
Laboratory of Physical Chemistry of Inorganic Materials (LPCMI), Faculty of Sciences Ain chock, University of Hassan II Casablanca, Morocco

Krimi Saida |
Laboratory of Physical Chemistry of Inorganic Materials (LPCMI), Faculty of Sciences Ain chock, University of Hassan II Casablanca, Morocco

Oudadesse Hassane |
University of Rennes, CNRS, ISCR-UMR 6226, F-35000 Rennes, France

نشانی اینترنتی https://www.physchemres.org/article_135170_f4ab38dfff65ea77e8c1a58bee37fc70.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات