عنوان انگلیسی Chemical State Analysis of Magnesium-Supported Ziegler-Natta Catalyst by Soft X-ray Emission Spectrometer (SXES) after Contact with Alkyl Aluminum
چکیده انگلیسی مقاله This report is on the characterization of active Ti center in heterogeneous Ziegler-Natta catalysts with Soft X-ray Emission Spectrometer (SXES). Since titanium in the catalyst has various chemical bonds, it is important to grasp the chemical bond state. The outermost shell electrons are very important for understanding the chemical bond state. SXES is the only method that can easily observe outermost shell electrons with current analytical instruments. Here, a co-milled solid of MgCl2, TiCl4, and Phthalate was used as a catalyst precursor, and three types of catalysts with significantly different catalytic activity levels were synthesized by changing the subsequent preparation process. The correlation between catalytic activity and the signal shape of Lα,β emission, which is the outermost shell electron of Ti in SXES analysis, was investigated. Lα,β emission was detected as broad signal. It could be observed that the high active catalyst had relatively strong signal intensity at the high energy side.
   The shape changes were also checked when the catalyst solids were treated by triethylaluminium. By this treatment, the relative intensity of the high energy side signal was further enhanced, suggesting that triethylaluminium treatment induced the elimination of inactive Ti from the catalyst solid. By comparing with the solid 13C-NMR analyses data of the Ziegler-Natta catalyst described in our previous report, the high energy side signal of Ti Lα,β in SXES results implies the relationship with the NMR results for carbonyl function.
کلیدواژه‌های انگلیسی مقاله Ziegler-Natta catalyst, propene polymerization, soft X-ray emission spectrometry (SXES), field emission scanning electron microscopy (FE-SEM), polymerization activity, outermost shell electrons of titanium
نویسندگان مقاله Masayoshi Saito |
Analysis Center, Toho Titanium Co., LTD., 3-3-5, Chigasaki, Chigasaki-City, Kanagawa, 253-8510, Japan

Hiroshi Kashimura |
Analysis Center, Toho Titanium Co., LTD., 3-3-5, Chigasaki, Chigasaki-City, Kanagawa, 253-8510, Japan

Takuo Kataoka |
Analysis Center, Toho Titanium Co., LTD., 3-3-5, Chigasaki, Chigasaki-City, Kanagawa, 253-8510, Japan

Masahide Murata |
Former Toho Titanium Co., LTD, Japan

Yusuke Sakuda |
JEOL Ltd., 3-1-2 Musashino, Akishima, Tokyo 196-8558, Japan

Hiroyuki Yamada |
JEOL Ltd., 3-1-2 Musashino, Akishima, Tokyo 196-8558, Japan

Hideyuki Takahashi |
JEOL Ltd., 3-1-2 Musashino, Akishima, Tokyo 196-8558, Japan

نشانی اینترنتی http://poj.ippi.ac.ir/article_2029_9b7d20fd16e5e3f0166d5e23820345da.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات