عنوان انگلیسی Synthesis and Characterization of a Novel Nanoporous Composite Based on Elemental Sulfur and Graphitic Mesoporous Carbon
چکیده انگلیسی مقاله A novel sulfur nanocomposite was fabricated based on graphitic mesoporous carbon.The graphitic mesoporous carbon was synthesized using sucrose as carbon precursor, nano CaCO3 as hard template and nickel nitrate as graphitization catalyst. The structural properties of the prepared material were characterized using powder X-Ray Diffraction (XRD), N2-adsorption/desorption and Scanning Electron Microscopy (SEM) techniques. The mesoporous solid with high surface area of 710 m2/g, average pore size of 2.7 nm and high graphitization degree was applied as nanoreactor for infiltration of molten sulfur at 150 ºC in an inert gas atmosphere. The properties of prepared nanocomposite were investigated by XRD, BET, SEM and cyclic voltammetry methods. The obtained results showed that the desired nanocomposite with enhanced conductivity successfully was synthesized.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله
نشانی اینترنتی http://www.ijcce.ac.ir/article_23549_08ec7f0834acf6d6f392e7d53edc97da.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/444/article-444-315710.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات