عنوان انگلیسی Chemical, Physical and Mechanical Properties of Hybrid Foam Concrete Panels Made of Polyurethane and white Portland Cement
چکیده انگلیسی مقاله Indoor heat blockage panels are important wall material for energy saving and room convenience, especially in tropical regions. The panels are prepared from hybrid foam concrete made of various percentages of polyurethane (PUR), and white Portland cement (WCM). The properties were studied based on the chemical reaction mechanism, physical parameters, and mechanical characteristics. Hybrid foam is fabricated in the form of wall panels by mixing diphenylmethane-4,4'-diisocyanate and blended polyol consisting of ethylene glycol, catalyst, surfactant, and Portland white cement filler with varying PUR matrix composition. XRF, XRD, FT-IR, and SEM analyses were conducted to identify the reaction mechanism, both cementation and polymerization reactions. Thermal conductivity and thermogravimetry analysis were conducted to determine the thermal properties of the panels. The XRF analysis on WCM specimens deduced the Ca(OH)2 content of 81.366%, and XRD analysis of the hydration reaction recorded the presence of CSH at an angle of 2θ = 29o to 2θ = 35o, with insignificant crystallinity properties. In the percentage of 25% and 60% PUR, the porosities were 11.24% and 17.95%, respectively. It confirmed the density reduction from 1,251 kg/m3 to 1,100 kg/m3. The thermal conductivity decreased consistently as the percentage of PUR increased. The lowest thermal conductivity was recorded at 0.0882 W/mK (PUR 60%). At 60% PUR, the compressive strength ranged from 5 to 8 MPa (7–28 days of curing time). Thermogravimetric behaviors of the PUR-WCM HFC showed that the two-stage decomposition peaks; at 373 K and 596 K, represented the dehydration of CSH and the decomposition of PUR. This material has the proper characteristics for a thermal insulation material since it has appropriate heat resistance, low thermal conductivity, and acceptable mechanical strength.
کلیدواژه‌های انگلیسی مقاله Hybrid foam concrete,Polyurethane matrix,White Portland cement,Mechanical properties,physical parameter,chemical reaction mechanism
نویسندگان مقاله Jofrishal Jofrishal |
Graduate School of Mathematics and Applied Science, Universitas Syiah Kuala, Banda Aceh, 23111, INDONESIA

Muhammad Adlim |
Graduate School of Mathematics and Applied Science, Universitas Syiah Kuala, Banda Aceh, 23111, INDONESIA

Elin Yusibani |
Physics Department, Faculty of Mathematics and Natural Sciences, Universitas Syiah Kuala, Banda Aceh, 23111, INDONESIA

Akhyar Akhyar |
Mechanical Engineering Department, Faculty of Engineering, Universitas Syiah Kuala, Banda Aceh, 23111, INDONESIA

Ratu Fazlia Inda Rahmayani |
Chemistry Department, Faculty of Teacher Training and Education, Universitas Syiah Kuala, Banda Aceh, 23111, INDONESIA

Rahmatul Fajri |
Chemistry Department, Faculty of Engineering, Universitas Samudra, Langsa, 24415, INDONESIA

نشانی اینترنتی https://ijcce.ac.ir/article_706306_cc887b04ca1887a7b5023320180a21c4.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات