عنوان انگلیسی Surface-initiated Atom Transfer Radical Polymerization and Solution Intercalation Methods for Preparation of Cellulose-G-PS-G-PAN/MMT Bionanocomposite
چکیده انگلیسی مقاله Cellulose was modified by polystyrene (PS) and polyacrylonitrile (PAN) via free radical and living radical polymerization, and then cellulose was used as the matrix in the preparation of polymer/clay nanocomposite, through a solution intercalation method. For this purpose, first, the graft polymerization of styrene (St) onto cellulose fibers was performed by using suspension polymerization and the free-radical polymerization technique in the presence of potassium persulfate (PPS). Second, the synthesized cellulose-graft-polystyrene was brominated by N-bromosuccinimide (NBS) to obtain polymers with bromine a group. Third, the brominated cellulose fibers were used as macroinitiators in the atom transfer radical polymerization (ATRP) of acrylonitrile (AN) in the presence of CuCl / 2, 2’-bipyridine (Bpy) catalyst system in THF solvent at 90˚C to prepare the cellulose-graft-polystyrene–graft–polyacrylonitrile. Forth, for preparing the modified clay, Na-MMT was mixed with hexadecyl trimethyl ammonium chloride salt. Finally, cellulose-graft-polystyrene–graft–polyacrylonitrile/organoclay bionanocomposite was prepared in CCl4 by a solution intercalation method. Then, the structure of the obtained terpolymer was investigated by FT-IR, DSC, TGA, XRD, and SEM techniques. Moreover, the structure of the bionanocomposite was probed by XRD, SEM, and TEM images.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله موسی پاکزاد |
zanjan university
سازمان اصلی تایید شده: دانشگاه زنجان (Zanjan university)

علی رمضانی |
faculty of science, university of zanjan, zanjan, iran
سازمان اصلی تایید شده: دانشگاه زنجان (Zanjan university)

مجتبی عباسیان |
payame noor university
سازمان اصلی تایید شده: دانشگاه پیام نور تهران (Payame noor university)

نشانی اینترنتی http://jpst.ripi.ir/article_705_c6603a64210c286ae8f76dd03355e996.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/504/article-504-324423.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات