عنوان انگلیسی Fabrication and Valuation of a PLA Nanocomposite Membrane: Mechanical, Thermal Stability, and Biodegradability
چکیده انگلیسی مقاله Although polylactic acid PLA has excellent properties such as good biocompatibility, excellent transparency, and non-toxicity for membrane synthesis, it has disadvantages such as poor mechanical properties, low elongation at break, low elasticity, and slow crystallization rate. To change the properties of PLA membranes, it would be effective to blend other biopolymers and fillers with PLA. In the present work, a biopolymer composite membrane was prepared by blending polybutylene succinate and polypropylene carbonate and then mixed with polyhydroxybutyrate and silica nanoparticles. Finally, it was combined with PLA. It is seen that the produced membranes had better elongation at break and lower tensile strength than pure PLA. The results of past work have shown that the PLA-containing biopolymers decrease the thermal stability because of the lower T. In contrast, the thermal stability increased when the biopolymers included silica NPs. Outcomes of biodegradability revealed that the composite membranes have better biodegradability than pure PLA. The weight loss of membranes without NPs was 38% and 49% under anaerobic and aerobic, respectively. In comparison, the weight loss of biopolymer-NPs membrane was obtained as 33% and 43% under anaerobic and aerobic, respectively.
کلیدواژه‌های انگلیسی مقاله biopolymer,poly (lactic acid),Composite membrane,Biodegradable Membrane
نویسندگان مقاله Mohammad Ghorbani |
Department of Chemical Engineering, Shahreza Branch, Islamic Azad University, Shahreza, I.R. IRAN

Mohammad Hassan Vakili |
Department of Chemical Engineering, Shahreza Branch, Islamic Azad University, Shahreza, I.R. IRAN

Elham Ameri |
Department of Chemical Engineering, Najafabad Branch, Islamic Azad University, Najafabad, I.R. IRAN

نشانی اینترنتی https://ijcce.ac.ir/article_714322_99bda5a13c71f7eba089abb36bdd9c86.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات