Iranian Journal of Chemistry and Chemical Engineering، جلد ۴۴، شماره ۱، صفحات ۱-۱۶
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Development of a 3D Bioprinted Alginate-Gelatin Hydrogel Scaffold Loaded with Calcium Phosphates for Dental Pulp Tissue Regeneration
چکیده انگلیسی مقاله Dental pulp restoration using hydrogel is an innovative approach that offers enhanced biocompatibility and regenerative potential. Hydrogels, with their three-dimensional structure and ability to mimic the natural ExtraCellular Matrix (ECM), show a favorable environment for regenerating damaged pulp tissue. Alginate and gelatin were combined to form the hydrogel matrix. CaPs were added at 0 wt%, 2 wt%, 4 wt%, and 6 wt% to investigate the effects on the hydrogel's properties and potential for dental pulp regeneration. Characterization techniques included X-Ray Diffraction (XRD), and Scanning Electron Microscope (SEM) to analyze the morphological, and surface properties of the alginate-gelatin-CaP hydrogels. Cell activity and viability were assessed using the MTT assay. The mechanical properties of the alginate-gelatin hydrogel samples containing 0, 2, 4, and 6 wt% CaPs were evaluated using finite element analysis. Machine learning (ML) techniques were employed to model the relationship between the CaP content and the hydrogel's compressive, tensile, and viscoelastic behaviors, enabling the prediction of optimal CaP loading for desired mechanical characteristics. The present study utilized ML techniques to investigate the interrelationships among various parameters and forecast their corresponding effect. Specifically, ML algorithms were employed to estimate the pH change, degradation, weight gain, and initial diameter based on fluctuations in weight fraction, compressive strength, and porosity. Furthermore, the accuracy of the ML-based predictions was validated through the application of linear regression analysis, which confirmed the model's reliability. The results showed that increasing CaP content in the alginate-gelatin hydrogel improved the compressive strength, reduced porosity, and enhanced pH stability, while increasing degradation and weight gain, with an optimal 4 wt% CaP range. The incorporation of 4 wt% CaPs into the alginate-gelatin hydrogel matrix enhanced the mechanical properties, bioactivity, and stability, highlighting the potential of this nanocomposite scaffold for applications in dental pulp tissue engineering.
کلیدواژه‌های انگلیسی مقاله 3D bioprinting,Alginate-gelatin hydrogel,Calcium phosphates (CaPs),Dental pulp restoration,Biomechanical properties
نویسندگان مقاله Abbasali Khademi |
Department of Endodontics, Dental Research Center, Dental Research Institute, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, I.R. IRAN

Amirsalar Khandan |
Department of Endodontics, Dental Research Center, Dental Research Institute, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, I.R. IRAN

Pedram Iranmanesh |
Department of Endodontics, Dental Research Center, Dental Research Institute, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, I.R. IRAN

Mahboobeh Heydari |
Medical Information, Dental Implants Research Center, Dental Research Institute, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, I.R. IRAN

نشانی اینترنتی https://ijcce.ac.ir/article_715938_51589b3550b6c130f8ab4ee78647179f.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات