Iranian Journal of Materials Forming، جلد ۱۱، شماره ۴، صفحات ۱۸-۲۶
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی The Effects of Multi-Walled Carbon Nanotubes on the Mechanical Properties of Silicone Rubber-Based Nanocomposites
چکیده انگلیسی مقاله In this study, multi-walled carbon nanotubes (MWCNTs) were used as reinforcement for silicone rubber at different weight percentages (i.e. 0, 0.25, 0.5, and 1 wt.%). The tensile, compressive, and compression set behaviors of the prepared composites were examined through standard tests. The fracture surface of the tensile samples was also analyzed using a scanning electron microscope (SEM). The results indicate that incorporating 0.25 wt.% MWCNTs into silicone rubber leads to an 11% increase in tensile strength and a 27% increase in elastic modulus compared to pure silicone rubber. Furthermore, the presence of MWCNTs nanoparticles enhances the compressive strength from 3.2 MPa in pure silicone to 6.2 MPa at 0.25 wt.%, while increasing the MWCNT content up to 1 wt.% gradually decreases the compressive strength. Additionally, the presence of MWCNTs reduces the compression set of silicone rubber.
کلیدواژه‌های انگلیسی مقاله Silicone Rubber,multi-walled carbon nanotube,Tensile properties,compressive strength,Compression set
نویسندگان مقاله R. Mashi |
Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran

S.M. Zebarjad |
Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_7937_c0f1e6d164ddf385b0d3c0aafc71105d.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات