International Journal of Mining and Geo-Engineering، جلد ۵۹، شماره ۳، صفحات ۲۰۱-۲۱۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Extraction of nickel from spent reforming catalyst through bioleaching with mesophilic and moderately thermophilic cultures
چکیده انگلیسی مقاله Considering the strategic relevance of nickel in a variety of industries, it is crucial to discover a method for extracting it from secondary sources. Spent reforming catalysts are hazardous to the environment, and require proper waste management techniques. In this research, the extraction of nickel from spent catalysts was studied and it was discovered that this process can dissolve a significant amount of nickel. Due to the high calcite content in the sample, its dissolution led to an elevation in pH, which negatively impacted bioleaching. It was observed that when the sample was added to the bioleaching solution after bacterial growth, the pH of the solution elevated less, and recovery improved. Moderately thermophilic bacteria had a better capability to reduce the pH and showed 66% nickel recovery which was slightly higher than the 61% recovery observed with mesophilic bacteria. Leaching tests and XRD analysis revealed that the portion of the nickel that is in the NiO phase is resistant to conventional leaching or bioleaching treatment, but reducing the sample with H2 as the pretreatment process can enhance the recovery of nickel. Reductive pretreatment of the sample can improve recovery, however it is not advised since it may have adverse environmental implications. The toxicity assessment test revealed that the bioleaching process with both cultures is able to reduce the risk of catalyst waste.
کلیدواژه‌های انگلیسی مقاله Bioleaching,Mesophile,Thermophile,Reforming catalyst,nickel
نویسندگان مقاله Hadi Abdollahi |
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran.

Esmaeel Talebi |
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran.

Roozbeh Saneie |
Department of Materials Engineering, The University of British Columbia, Vancouver, Canada.

Ali Rezaei |
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran.

Minoo Ghanbarzad |
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran.

Fatemeh Maleki |
School of Mining Engineering, College of Engineering, University of Tehran, Tehran, Iran.

Sara Magdouli |
Department of Civil Engineering, University of Ottawa, Ottawa, ON, Canada.

نشانی اینترنتی https://ijmge.ut.ac.ir/article_102882_a392915e04d52a3365cf5a46f8456053.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات