Iranian Journal of Materials Forming، جلد ۱۲، شماره ۴، صفحات ۳۴-۴۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Microstructure and mechanical properties of Al-TiC composite fabricated by accumulated extrusion bonding (AEB)
چکیده انگلیسی مقاله There is a growing demand for the use of light metals such as Al and its alloys in various industrial applications due to their high strength-to-weight ratio. Many studies were conducted to improve their properties by developing fine-grained structures and/or adding reinforcing particles. In this study, Al-TiC composite samples were fabricated using the accumulated extrusion bonding (AEB) method, which is a severe plastic deformation technique. The effects of particle volume fraction and the number of extrusion passes on the microstructure and mechanical properties of the composites were investigated. The results indicated that the AEB of the pure Al sample at 390°C with a 90% reduction in cross-sectional area resulted in proper interlayer bonding. The composite samples were fabricated by incorporating varying content of TiC particles (0.5, 1, and 2 vol.%) between the layers. It was found that the strength and hardness of the composite increased with the volume fraction of reinforcing particles. After four AEB passes, the composite sample containing 2 vol.% TiC exhibited a uniform distribution of TiC particles, resulting in an 83% increase in tensile strength and a 156% increase in hardness compared to the annealed sample.
کلیدواژه‌های انگلیسی مقاله Aluminum composite,TiC,accumulated extrusion bonding,Mechanical properties
نویسندگان مقاله Ali Jafari |
Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran

Nozar Anjabin |
Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_8287_e35a19ce19a998d90595de041d26fc3b.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات