عنوان انگلیسی EFFECT OF POST-DEFORMATION ANNEALING TREATMENT ON INTERFACE PROPERTIES AND SHEAR BOND STRENGTH OF Al-Cu BIMETALLIC RODS PRODUCED BY EQUAL CHANNEL ANGULAR PRESSING
چکیده انگلیسی مقاله Effects of annealing treatment after equal channel angular pressing (ECAP) on the interface properties and shear bond strength of Al/Cu bimetallic rods were investigated. For the as-deformed samples, the one with two passes of ECAP indicated higher shear bond strength. Formation of a layer of intermetallic compounds after annealing treatment is confirmed. In general, by increasing annealing temperature, thickness of intermetallic compounds at the interface increases. Shear bond strength was initially reduced by annealing at 200, 250 and 300 ͦ C and increased at 350 ͦ C. With further increase in annealing temperature to 400 ͦ C, shear bond strength slightly decreased which is correlated to the increased thickness of the intermetallic compounds.
کلیدواژه‌های انگلیسی مقاله Bimetallic rod, Annealing, Interface, Shear bond strength.
نویسندگان مقاله حمیدرضا mirzakouchakshirazi | hamid reza mirzakouchakshirazi
narmak


علیرضا ایوانی | ali reza eivani
narmak


شهرام خیراندیش | shahram kheirandish
narmak
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-779-2&slc_lang=en&sid=en
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/454/article-454-432688.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مکانیکی و شکل دادن
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات