عنوان انگلیسی Adsorption and Desorption Process of Chromium Ions Using Magnetic Iron Oxide Nanoparticles and Its Relevant Mechanism
چکیده انگلیسی مقاله In this study adsorption of Cr(VI) from aqueous solution by Fe3O4 nanoparticles was investigated. Desorption process and recovery of nanoparticles using different solutions were then carried out, and it was observed that NaOH (0.5M) can remove 90% of adsorbed chromium ions. Following the completion of adsorption/ desorption cycles, it was determined that nanoparticles have still had a high ability of chromium ions adsorption after 4 cycles. In addition, it was found that when iron oxide nanoparticles were washed with NaOH solution, the adsorption efficiency increases in the next cycle. FTIR spectra and zeta potential analysis, demonstrated the increased in surface positively charged of nanoparticles leads to increased electrostatic attraction forces between the iron oxide nanoparticles and chromium ions which finally resulted in adsorption increasing. So in this research, pretreatment of nanoparticles with NaOH solution modifies the surface of Fe3O4 nanoparticles by increasing surface positively charged mechanism and the adsorption efficiency has improved in the next cycle.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m جدیدی |
department of chemical engineering, isfahan university of technology, isfahan, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

n اعتصامی |
department of chemical engineering, isfahan university of technology, isfahan, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

m نصراصفهانی | nasr esfahany
department of chemical engineering, isfahan university of technology, isfahan, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

نشانی اینترنتی http://www.ijche.com/article_51449_477b49f98e33354aacbeccb3811e3236.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/443/article-443-485030.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات