Iranian Journal of Materials Forming، جلد ۴، شماره ۲، صفحات ۲۵-۳۶
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی The Effect of Hot Deformation Parameters on Grain Size Refinement in a Martensitic Stainless Steel
چکیده انگلیسی مقاله The grain size refinement of AISI 422 martensitic stainless steel in the temperature range of 950-1150 ºC was investigated by hot deformation tests. The deformed specimens were held at deformation temperature with delay times of 5 to 300s after achieving a strain of 0.3. The austenite grains exhibit a considerable growth at temperature higher than 1050˚C, while the grain coarsening is negligible at lower deformation temperatures. Therefore, it is a difficult task to achieve a fine grain structure at these high deformation temperatures. In the second stage of this work, the grain growth behavior of the deformed alloy at temperature range of 940-1020 ºC was investigated to obtain a fine austenite grain in the final deformation step. A uniform and fine-grain structure, with average grain size less than 30 µm, can be obtained by considering the appropriate temperature and strain per pass. At 1020˚C a relatively fine and uniform recrystallized grain, mean grain size of about 28 µm, is obtained with an applied strain of 0.4, while at 980˚C after strain of 0.2 a nearly equiaxed grain with the same mean grain size is achieved.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله r محمدی احمدآبادی | mohammadi ahmadabadi
amirkabir university of technology
سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

m نادری |
department of mining and metallurgical engineering, amirkabir university of technology
سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

j آقازاده مهندسی | aghazadeh mohandesi
ِdepartment of mining and metallurgical engineering, amirkabir university of technology
سازمان اصلی تایید شده: دانشگاه صنعتی امیرکبیر (Amirkabir university of technology)

j cabrera |
departamento de ciencia de los materiales e ingenier amp;iacute;a metal amp;uacute;rgica, etseib, universitat polit amp;eacute;cnica de catalunya

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_4290_fe9ce8486f741bead5b936ccd6e85c4f.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/453/article-453-494724.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات