Polyolefins Journal، جلد ۵، شماره ۱، صفحات ۱۵-۲۲
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Synthesis of cyclic olefin polymers with high glass transition temperature and high transparency using tungsten-based catalyst system
چکیده انگلیسی مقاله Novel cyclic olefin polymers (COPs) derived from bulky cyclic olefins, tricyclodipentadiene (TCPD) and tricyclo[6.4.0.19,12]-tridec-10-ene (TTE), with high glass transition temperature (Tg), excellent thermal stability, and high transparency, have been synthesized by ring-opening metathesis polymerization (ROMP) and subsequent hydrogenation. ROMP of TCPD and TTE was carried out successfully without gel formation using a WCl6/i-Bu3Al/Et-OH/hexene catalyst system at room temperature. By changing the TCPD/TTE molar ratio, the optimized catalyst component ratio for the polymerization varied. Chemical structures of the unsaturated and hydrogenated polymers were characterized by 1H NMR technique. Thermal properties of these newly synthesized polymers were determined using TGA and DSC measurements. The degradation temperatures (Td) were all above 420°C in N2, indicating that all these copolymers had excellent thermal stability. After hydrogenation, Tg of ROMP polymers was decreased by 30-60°C. The Tg of h-pTCPD reached as high as about 230°C. The light transmittances of these polymer films were also analyzed using UV-Vis absorption spectroscopy. A high light transmittance of up to 92% was found by UV-Vis absorption spectra for these polymer films.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله lei cui |
state key laboratory of polymer physics and chemistry, changchun institute of applied chemistry, chinese academy of sciences, changchun 130022, china

ji xing یانگ | ji xing
school of material science and engineering, tianjin university, tianjin 300350, china

یان گیو li | yan guo
state key laboratory of polymer physics and chemistry, changchun institute of applied chemistry, chinese academy of sciences, changchun 130022, china

yue sheng li | yue sheng
school of material science and engineering, tianjin university, tianjin 300350, china

نشانی اینترنتی http://poj.ippi.ac.ir/article_1476_c0c51a0bdf7a7067c05dc434e71418ab.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/531/article-531-539313.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات