عنوان انگلیسی Electrosynthesis, Characterization and Corrosion Inhibition Study of DBSA-doped Polyaniline Coating on 310 Stainless Steel
چکیده انگلیسی مقاله The synthesis of polyaniline doped with dodecylbenzene sulphonic acid (Pani-DBSA) coatings on 310 stainless steel (310 SS) surfaces has been investigated by using the galvanostatic method. The synthesized coatings were characterized by Fourier Transform Infrared Spectroscopy (FT-IR), UV-Visible absorption spectrometry and Scanning Electron Microscopy (SEM).The anticorrosion performances of PAni-DBSA coatings were investigated in 5% NaCl solution by the potentiodynamic polarization technique and Electrochemical Impedance Spectroscopy (EIS). The corrosion rate of Pani-DBSA coated 310 SS was found ∼30 times lower than bare 310 SS and potential corrosion increased from -0.84 V versus Ag/AgCl for uncoated 310 SS to -0.71 V versus Ag/AgCl for Pani-DBSA coated 310 SS electrodes. Electrochemical measurements indicate that Pani-DBSA coated have good inhibiting properties with mean efficiency of ~96% at 5 mA cm-2 current density applied on 310 SS corrosion in chloride media. The results of this study clearly ascertain that the Pani-DBSA has an outstanding potential to protect 310 SS against corrosion in a chloride environment.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله یاسر جعفری |
department of analytical chemistry, faculty of chemistry, university of kashan, kashan, i.r. iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

سید مهدی قریشی | sayed mehdi
department of analytical chemistry, faculty of chemistry, university of kashan, kashan, i.r. iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

مهدی شعبانی آبادی | shabani nooshabadi
department of analytical chemistry, faculty of chemistry, university of kashan, kashan, i.r. iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

نشانی اینترنتی
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات