Journal of Computational and Applied Research in Mechanical Engineering - JCARME، جلد ۷، شماره ۲، صفحات ۱۷۵-۱۸۷
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Effect of relative humidity on mechanical strength of zirconia/ Nafion® Nano-composite membrane
چکیده انگلیسی مقاله This paper presents the results of mechanical strength of wet and dry zirconia/ Nafion® nano-composite membrane. The tensile tests were conducted to determine elastic modulus and stiffness of dry and wet pristine Nafion® membrane and modified Nafion® membrane. The composite membranes were prepared by recast method of different synthesized zirconium oxide with the zirconia content of 10% by weight. The uniaxial mechanical properties of nano-composite membranes and recast Nafion® membrane were captured using a CellScale UStretch uniaxial testing system. The length, width, and thickness of samples were measured using a Vernier caliper and recorded prior to testing. It was found that elastic modulus of the wet Nafion recast is 62.06 %, 35.26 %, 30.79 % and 35.26 % higher than that of Nafion®/ Zr-100, Nafion/® Zr-80, Nafion®/Zr-50, and Nafion®/Zr-0, respectively. The elastic modulus of dry Nafion recast, Nafion®/Zr-100, Nafion®/Zr-80, Nafion®/Zr-50, and Nafion/Zr-0 membranes are 46.29 %, 83.31 %, 64.81 %, 59.84 %, and 78.36 % higher than those of wet Nafion® recast, Nafion®/Zr-100, Nafion®/Zr-80, Nafion®/Zr-50, and Nafion®/Zr-0 membranes, respectively. Furthermore, the results showed that when the water content increases in the nano-composite membranes the mechanical strength also decreases.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله Fulufhelo Nemavhola |
University of South Africa Department of Mechanical and Industrial Engineering

Simon Dhlamini |
University of South Africa

Rudzani Sigwadi |
University of South Africa

Touhami Mokrani |
University of South Africa

نشانی اینترنتی http://jcarme.srttu.edu/article_764_5898d8a73a2a6c0deae97412217e50e6.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/484/article-484-577202.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات