عنوان انگلیسی Comparison of push-out bond strength of mineral trioxide aggregate and calcium enriched mixture cement as root end fi lling materials
چکیده انگلیسی مقاله Background: The purpose of this study was to compare the push-out bond strength of mineral trioxide aggregate (MTA) and calcium enriched mixture (CEM) as root end fi lling materials. Materials and Methods: A total of 40 root dentin slices (1 ± 0.2 mm) were prepared from freshly extracted human maxillary central teeth and their lumens were enlarged to 1.3 mm. The slices were randomly divided into two groups (n = 20). MTA and CEM cement were mixed according to manufacturer’s instruction and introduced into the lumens. The specimens were wrapped in pieces of wet gauze soaked in distilled water and incubated at 37°C for 3 days. The push-out bond strength was measured using a universal testing machine. The slices were then examined under a light microscope at ×10 magnifi cation to determine the nature of bond failure. The data were analyzed using Mann-Whitney test (P < 0.001). Results: The mean push-out bond strength for CEM cement and MTA were 1.68 ± 0.9 and 5.94 ± 3.99 respectively. The difference was statistically signifi cant (P < 0.001). The bond failure was predominantly of adhesive type in MTA group and cohesive type in CEM group. Conclusion: CEM cement showed signifi cantly lower bond strength to the dentinal wall compared to MTA. Key Words: Adhesive, calcium enriched mixture cement, cohesive, mineral trioxide aggregate, push-out bond strength
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله علیرضا عدل | alireza adl


فرشته صبح نمایان | fereshte sobhnamayan


امید کاظمی | omid kazemi


نشانی اینترنتی http://drj.mui.ac.ir/index.php/drj/article/view/1627
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article(s)
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات