عنوان انگلیسی Fabrication of PGS/CaTiO3 Nano-Composite for Biomedical Application
چکیده انگلیسی مقاله Biodegradable elastomeric materials are gaining extensive attention in the field of soft tissue engineering. Poly (glycerol sebacate) (PGS) is a novel biocompatible elastomer in this scope. However this polymer has poor mechanical properties especially when the molar ratio of glycerol is higher than sebacic acid. Calcium Titanate (CaTiO3) is a biocompatible ceramic with some degrees of piezoelectricity, which is in favor of cell growth. In this study; Calcium Titanate is synthesized at nano-scale by sol-gel method and dispersed into as-synthesized PGS pre-polymer in weight-ratio of 5:95 for CaTiO3 and PGS, respectively. This waxy material was cured to achieve the final product. The molar ratio of glycerol and sebacic acid for the synthesis of PGS was 1:0.8, respectively. X-ray diffraction (XRD) test confirms successful synthesis of CaTiO3 and the nano-scale of crystals are approved by transmission electron microscopy (TEM) Image. Fourier transform infrared (FTIR) spectroscopy has revealed a chemical bond between the two phases after addition of ceramic into pre-polymer. Distribution of CaTiO3 nano-structures in the polymeric matrix is shown by Scanning Electron Microscopy (SEM).
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله r ناصر |
biomaterial engineering group, isfahan university of medical sciences, isfahan, iran
سازمان اصلی تایید شده: دانشگاه علوم پزشکی اصفهان (Isfahan university of medical sciences)

a زرگر خرازی | zargar khrazi
biomaterial engineering group, isfahan university of medical sciences, isfahan, iran
سازمان اصلی تایید شده: دانشگاه علوم پزشکی اصفهان (Isfahan university of medical sciences)

gh دینی |
department of nanotechnology engineering, faculty of advanced sciences and technologies, university of isfahan, isfahan 81746-73441, iran
سازمان اصلی تایید شده: دانشگاه اصفهان (Isfahan university)

نشانی اینترنتی http://www.ijnnonline.net/article_20406_bed0406380793c9fd7dc42a8bf74a9ac.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات