International Journal of Nanoscience and Nanotechnology (IJNN)، جلد ۹، شماره ۳، صفحات ۱۳۹-۱۴۲
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Microwave–Assisted Hydrothermal Synthesis and Optical Characterization of SnO2 Nanoparticles
چکیده انگلیسی مقاله Semiconductor nanoparticles exhibit size dependent properties due to quantum confinement effect that are not present in their bulk counterparts. In this work, extremely fine and pure SnO2 nanoparticles of ~1.1 nm size were synthesized by a solution process, in which amorphous precipitate of SnO2 was crystallized by microwave heating. The particles sizes varied from ~1.1 to ~2.7 nm. By XRD analysis, the particle size, crystal structure and purity of the samples were determined. The UV-Vis measurements of SnO2 nanoparticles, showed that, excitonic peaks existed at ~237, ~250 and ~279 nm corresponding to ~1.1, ~2 and ~2.7 nm clusters respectively. The STM analysis showed that the nanoparticles were spherical in shape, having narrow size distribution.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله p بروجردیان |
department of passive defense, malek ashtar university of technology, tehran, i. r. iran.
سازمان اصلی تایید شده: دانشگاه صنعتی مالک اشتر (Malek ashtar university of technology)

نشانی اینترنتی http://www.ijnnonline.net/article_4010_3e42d36ef9fbbe6a88a96a613bc39c20.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات