عنوان انگلیسی EFFECT OF COMPOSITION ON PHASE EVOLUTION AND MICROSTRUCTURE OF REACTION BONDED MULLITE (RBM)
چکیده انگلیسی مقاله Compositions of Al2O3+Si, SiO2+Al and Al+Si systems were prepared to study the effect of reaction bonding process on the mullite formation. The composition of each system was adopted according to mullite stoichiometery and sintered in 700-1600°C range. Results showed that the formation of reaction bonded mullite starting from Al2O3+Si mixtures, proceeded in two partially overlapping steps, the oxidation of Si to SiO2, and the reaction of SiO2 and Al2O3 to form mullite. In this system, up to 1400°C, conversion of Si to SiO2 was taken place and cristobalite formed, but mullite formation was not observed. Mullite phase started to form at 1450°C. Results indicated that complete reaction was not occurred up to 1600°C and 2 hours soaking time. XRD patterns of samples in Al+ SiO2 system showed that the reaction through sequences: (a) reduction of SiO2 by Al, (b) formation of a- Al2O3 and SiO2-rderived Si oxidation, and (c) mullite formation. X-ray diffraction patterns of heat-treated Al+Si system showed that reaction between Al and oxygen at 900°C was occurred with the reaction product being a- Al2O3 Oxidation of Si and formation of mullite were not detected in this system. SEM micrographs showed that both Al2O3+Si and SiO2+Al systems have similar microstructures, which consisted of a- Al2O3, mullite and free Si. The microstructures of the samples in Al+Si system consisted of a- Al2O3 free Al and Si with intermetallic Al-Si compound.
کلیدواژه‌های انگلیسی مقاله MULLITE, REACTION BONDING OROCESS, ALUMINA, SILICON, SILICA
نویسندگان مقاله صلاحی e | salahi e
ceramic department, materials and energy research center merc , tehran, iran


عبادزاده t | ebadzadeh t


moztar زاده f | moztar zadeh f


صولتی هشجین m | solati hashjin m


نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-1-62&slc_lang=fa&sid=en
فایل مقاله دریافت فایل مقاله
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه سرامیک
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات