عنوان انگلیسی Investigation of Ca on the microstructural evolution and porosity analysis of ZK60 alloy in as-cast and extruded conditions
چکیده انگلیسی مقاله This research work has been carried out to study the effect of different Ca contents (0.5, 1.0, 1.5, 2.0 and 3.0) on the microstructure and porosity content of ZK60 alloys. The samples were examined by the use of optical and scanning electron microscopy (SEM) to evaluate the modification efficiency of the alloy with different Ca concentrations. The cast specimens have been modified, homogenized and extruded at 350 °C at an extrusion ratio of 12:1. Experimental results showed that the addition of Ca brings about precipitation of a new phases and refines the as-cast grains. It was also found that the presence of Ca at higher concentrations (>2 wt. %) results in the formation of hard Ca-rich intermetallics segregated in cell boundaries. Hot-extrusion was found to be powerful in breaking the eutectic network and changing the size and morphology of Ca-rich intermetallics phase. By applying the extrusion process and increasing the Ca concentration (up to 2.0 wt. %) porosity percentage decreased from 13.62% to 6.34% and 7.11% to 3.89% for ZK60 and ZK60+3%Ca alloys, respectively.
کلیدواژه‌های انگلیسی مقاله ZK60 alloy, microstructures, Ca addition, extrusion
نویسندگان مقاله S. Moradnezhad |
Imam Khomeini International, University, Qazvin, Qazvin, Iran

A. Razaghian |
Imam Khomeini International, University, Qazvin, Qazvin, Iran

M. Emamy |
School of Metallurgy and Materials Engineering, University of Tehran, Tehran, Iran

R. Taghiabadi |
Imam Khomeini International, University, Qazvin, Qazvin, Iran

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_5193_e67eb19aac28053b6e96682a51574f7d.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/453/article-453-1557034.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات