عنوان انگلیسی Electrodeposited Co-Pi Catalyst on α-Fe2O3 Photoanode for Water-Splitting Applications
چکیده انگلیسی مقاله Optoelectronic properties of hematite (α-Fe2O3) as a photoanode and the required over-potential in photo-assisted water splitting has been improved by presence of Co-Pi on its surface. In order to increase the lifetime of the photogenerated holes and lower the applied bias, cobalt-phosphate (Co-Pi) on nanostructured α-Fe2O3 by electrodeposition was deposited. The nanostructure morphology of the α-Fe2O3 was confirmed by XRD and SEM. After depositing four different thicknesses of Co-Pi on α-Fe2O3, their photo-electrochemical (PEC) property was determined using linear sweep voltammetry (LSV) and chronoamperometry. The SEM and EDX results showed a complete coverage of Co-Pi on α-Fe2O3 and that the Co:P ratio was approximately 1:1.9 for the best produced catalyst. The highest performance of about 200 mV decrease in the onset potential was achieved for the 30-minutes electrodeposited sample. The Co-Pi/α-Fe2O3 catalyst showed an enhancement of 100% of photocurrent compared to the bare α-Fe2O3.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله M. Toghraei |
Material Science and Engineering Department, K. N. Toosi University of Technology, Tehran, Iran

H. Siadati |
Material Science and Engineering Department, K. N. Toosi University of Technology, Tehran, Iran

نشانی اینترنتی http://www.ije.ir/article_82274_cac9ac8a1e2969385cffb50a1e7f6682.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2061697.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات