Iranian Journal of Materials Science and Engineering، جلد ۱۷، شماره ۱، صفحات ۰-۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Hot Deformation of the Mn-Ni-Cr Alloy During Compression
چکیده انگلیسی مقاله In this paper a constitutive equation was considered for the isothermal hot compression test of the Mn-Ni-Cr alloy. The hot compression test was performed in the strain rate range of 0.001-0.1 s-1 and deformation temperature was varied from 700 to 900 °C. A considerable reduction in flow stress was observed regardless of the strain rate when temperature was increased from 700 to 750 °C. DTA and XRD evaluation revealed that the removal of Mn3Cr phase and formation of the single solid solution phase were the reason for the flow stress reduction. At the low deformation temperature (700°C) and the high strain rate (0.1 s-1), a partially recrystallized microstructure was observed; this was such that with increasing the temperature and decreasing the strain rate, a recrystallized microstructure was completed. Also, the relationships between flow stress, strain rate and deformation temperature were addressed by the Zener-Holloman parameter in the exponent type with the hot deformation activation energy of 301.07 KJ/mol. Finally, the constitutive equation was proposed for predicting the flow stress at various strain rates and temperatures.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله | Mohsen Sadeghi
Materials Engineering Department, Malek Ashtar University of Technology, Shahin Shahr, Iran


| Morteza Hadi
Department of Materials Science and Engineering, Golpayegan University of Technology, Golpayegan, Iran


| Omid Bayat
Department of Materials science and Engineering, Hamedan University of Technology, Hamedan, Iran


| Hadi Karimi
Materials Engineering Department, Malek Ashtar University of Technology, Shahin Shahr, Iran.
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-2324-1&slc_lang=en&sid=1
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/454/article-454-2247295.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مکانیکی و شکل دادن
نوع مقاله منتشر شده Research paper