عنوان انگلیسی Kinetic Study of Niobium Carbide Coating Formation on AISI L2 Steel using Thermo-Reactive Deposition Technique
چکیده انگلیسی مقاله In the present study, Thermo-Reactive Deposition method (TRD) in a molten bath was used to form niobium carbide coating on AISI L2 steel. The coating was formed in five different composition of borax (Na2B4O7), boric acid (B2O3), and ferro-niobium. For all of the five compositions of molten bath, niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4 and 8 hours. The thickness of coating ranged between 3.6 ± 0.1 µm to 33.6 ± 0.5 µm depending on the bath composition, treatment time, and temperature. Kinetic study of the formation of NbC coating demonstrated that for the molten baths containing 10 wt.% ferro-niobium or more, growth of the coating is under the controled of by diffusion. For such molten baths, the activation energy of the process was estimated to be 122.5 kJ/mol. A practical formula to estimate the coating thickness in these molten baths has been suggested.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله Mohammad Azizi |
Materials and Metallugy Engineering, Iran University of Science and Technology (IUST)

نشانی اینترنتی http://www.ije.ir/article_71835_b946bace91c2ef4e9bcfdc5e0d2ad82c.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2422132.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات