عنوان انگلیسی Effect of zinc oxide nanoparticles on physical and antimicrobial properties of resin‑modified glass ionomer cement
چکیده انگلیسی مقاله Background: To improve the limitations, many modifications in the resin‑modified glass ionomer (RMGI) composition have been proposed. In this study, we evaluated the effect of different concentrations of zinc oxide (ZnO) nanoparticles incorporated into RMGI cement on its physical and antimicrobial properties. Materials and Methods: In this in vitro study, ZnO nanoparticles with 0–4 wt.% concentrations were incorporated into RMGI. The following tests were carried out: (a) Antibacterial activity against Streptococcus mutans tested by disc diffusion method, (b) mechanical behavior assessment by measuring flexural strength (FS) and flexural modulus (FM), (c) micro‑shear bond strength (μ‑SBS), and (d) fluoride and zinc release. Data were analyzed using the statistical tests of ANOVA, t‑test, and Tukey’s HSD post hoc in SPSS V22. The level of significancy was 0.05. Results: In the disc diffusion method, specimens with 2 wt.% ZnO nanoparticles showed the highest antimicrobial efficacy (P < 0.05). After 1 month of water storage, no significant difference was observed in FS and FM of the samples (P > 0.05). In 2 wt.% ZnO nanoparticles group, μSBS increased in the first 7 days but decreased by 17% after one month, which showed a significant difference with that of the control group. The fluoride release did no change in the ZnO nanoparticle‑containing group compared with the control group at all time intervals. Conclusion: Incorporation of 2 wt.% ZnO nanoparticles into the RMGI cement adds antimicrobial activity to the cement without sacrificing FS and fluoride release properties, while decreased μSBS. Key Words: Flexural strength, fluorides, glass ionomer cements, microbial sensitivity tests, zinc oxide
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله | Zahra Malekhoseini


| Mohammad Bagher Rezvani


| Mohammad Niakan


| Mohammad Atai


| Mahshid Mohammadi Bassir


| Hamid Safar Alizade


| Saba Siabani


نشانی اینترنتی http://drj.mui.ac.ir/index.php/drj/article/view/2239
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده Original Article(s)
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات