Iranian Journal of Materials Forming، جلد ۹، شماره ۱، صفحات ۱۳-۲۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Plastic Deformation of Nano-Single Crystal Co-Cr-Ni- Fe-Mn High Entropy Alloy in Tension From 10 K to 1000 K by Atomistic Simulations
چکیده انگلیسی مقاله The plastic deformation behavior of nano-single crystals of the equiatomic CoCrNiFeMn high entropy alloy (HEA) with the face-centered cubic structure has been studied in tension as a function of temperature from 10 K to 1000 K using atomistic simulations. It was found that the critical stress for the slip was decreased with the increase in temperature. The results showed that the temperature had a substantial effect on the deformation mechanism. Intrinsic stacking faults and dislocations observed extensively at 10 K but not substantially at a temperature of 1000 K. Plastic deformation at a temperature of 10 K has occurred by means of partial dislocations slip whereas slip and amorphization is observed at 1000 K.
کلیدواژه‌های انگلیسی مقاله High entropy alloy, Nano-crystal, deformation, phase transformation, Amorphization
نویسندگان مقاله Roghayeh Mohammadzadeh |
Department of Materials Engineering, Azarbaijan Shahid Madani University, Tabriz, Iran

Akbar Heidarzadeh |
Department of Materials Engineering, Azarbaijan Shahid Madani University, Tabriz, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_6499_bf8eba30cdcfaa13050ff5ec9eb1cdea.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات