عنوان انگلیسی Enhancement of E-glass fiber/epoxy composite bending performance via graphene addition
چکیده انگلیسی مقاله This paper presents an experimental investigation using graphene nanoplatelets (GnPs) to enhance the bending performance of E-glass fiber/epoxy composites. Each specimen was prepared with two layers of E-glass chopped strand mat via the hand lay-up technique and using various contents of GnPs in the matrix (0.1, 0.2, 0.3, 0.4 and 0.5 wt%). Mechanical and ultrasonic stirring methods were employed to disperse the GnPs in the matrix. The obtained results demonstrated that the highest increases of 23% and 26% in the flexural strength and modulus, respectively, were observed for the composite containing 0.4 wt% GnPs. With the incorporation of 0.1 wt% GnPs, the flexural failure strain of the composite was enhanced by 16% compared to the control composite. The evaluation of the fractured surfaces clearly demonstrated that the interface between the glass fiber and polymeric matrix was improved when GnPs were added into the matrix.
کلیدواژه‌های انگلیسی مقاله Fiber-reinforced composite, Graphene nanoplatelets, Bending performance, fracture surface
نویسندگان مقاله Mohammad Imanparast |
Department of Mechanical Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran

Hamed Khosravi |
Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran

نشانی اینترنتی https://jpst.irost.ir/article_1009_13d5c5c3b00ab7ce07096f258f7dc3bb.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات