عنوان انگلیسی Structural, Morphological and Physiochemical Analysis of SiC8H20O4/C2H5O/C7H16 Modified Mesoporous Silica Aerogels
چکیده انگلیسی مقاله Silica Aerogels are widely recognized and have grown a considerable interest among researchers due to their unique properties. Using Rice Husk Ash as the main precursor and Ambient Pressure Drying, the present study synthesized and compared 4 different mesoporous silica aerogel variants by independently modifying them with TEOS (SiC8H20O4), Ethanol (C2H5O) and n-Heptane (C7H16). The variants were characterized through BET, SEM, EDX and XRD respectively. As per results, the highest porosity %, surface area, pore volume, average pore size and lowest volume shrinkage of 85%, 312 m2/g, 0.76 cm3/g, 9.6 nm and 91.16% were observed in sample treated separately with TEOS, ethanol and n-heptane (SGTEH-Iso). However, the sample treated with simultaneous solvent exchange/n-heptane aging (SGTEH-Sim) followed next with 79.5%, 298 m2/g, 0.75 cm3/g, 9.2 nm and 91.86% respectively. Moreover, TEOS, ethanol and n-heptane were shown to enhance silica purity, strengthen gel network and suppress crack formation during ambient pressure drying. Finally, due to their high porosity, pore volume and average pore size, variants SGTEH-Iso and SGTEH-Sim can have potential application as adsorbents for heavy metal removal from wastewater.
کلیدواژه‌های انگلیسی مقاله Silica Aerogel,Sol-gel method,Rice Husk Ash,Ambient pressure drying,Mesoporous
نویسندگان مقاله Faheem Akhter |
Department of Chemical Engineering, Quaid-e-Awam University of Engineering, Science and Technology, Nawabshah, Pakistan. Department of Chemical Engineering, Mehran University of Engineering and Technology, Jamshoro, Pakistan

Dr. Suhail Ahmed Soomro |
Department of Chemical Engineering, Mehran University of Engineering and Technology, Jamshoro, Pakistan

Abdul Rauf Jamali |
Materials Engineering Department, NED University of Engineering and Technology, Karachi, Pakistan

Vassilis J Inglezakis |
Chemical and Process Engineering Department, University of Strathclyde, Glasgow, UK

نشانی اینترنتی https://www.physchemres.org/article_148826_bccb48b57dc519d243c2a800aba19684.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات