Iranian Journal of Materials Forming، جلد ۱۱، شماره ۱، صفحات ۲۴-۳۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی The Effect of Simple Shear Extrusion on the Microstructure and Surface Properties of Aluminum Components Produced by Powder Metallurgy
چکیده انگلیسی مقاله This study focuses specifically on the combination of two methods: powder metallurgy and severe plastic deformation. In this research, the influence of a single pass of simple shear extrusion (SSE) on the grain refinement, structural evolution, and some tribological properties of pure aluminum samples produced through the powder metallurgy method has been investigated. It is observed that after a single pass through the channel of SSE, the average grain size decreases, and the tribological properties of the sample significantly increases. The innovation of this research lies in the simultaneous combination of two methods: Fabrication of samples through powder metallurgy and severe plastic deformation. These methods lead to the alignment or even enhancement of the properties of the produced samples compared to conventionally cast samples. The recorded hardness values for the produced samples decreased from 57 Brinell for the as-cast sample to 29, 43, and 60.3 Brinell after initial pressing, sintering, and a single pass of SSE, respectively. Wear test results also indicate a substantial improvement in wear resistance in the refined-grain sample, with a weight loss reduction of 0.011 grams compared to the powder metallurgy stage. Furthermore, corrosion test results show an increase in corrosion potential from 730 to 720 millivolts in the powder metallurgy sample after SSE, and the current density decreases from 1.71 to 1.54 amperes per square centimeter in the powder metallurgy and simple shear extrusion samples, respectively.
کلیدواژه‌های انگلیسی مقاله aluminum, severe plastic deformation, Powder metallurgy, Simple Shear Extrusion, Wear
نویسندگان مقاله S.M. Sedehi |
School of Mechanical Engineering, College of Engineering, University of Tehran, Tehran, Iran

M. Samarghandi |
Department of Mechanical Engineering, Birjand University, Birjand, Iran

A. Samarghandi |
Department of Railway Engineering, Iran University of Science and Technology, Tehran, Iran

M. Maraki |
Department of Materials Engineering, Birjand University of Technology, Birjand, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_7526_094c61dcc803a58aa11a71a5e563cfdf.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات